655m13 grade steel is a nickel chromium alloy case hardening steel that is specified for heavy duty highly stressed applications.
En36a steel data sheet.
En36a case hardening steel typical analysis c si mn ni cr mo s p ave.
En36a is a 3 2 nickel chromium high hardenability case hardening carburizing steel generally supplied in the annealed condition with a maximum brinell hardness of 255 rc26.
832m13 grade steel is a nickel chromium alloy case hardening steel that is specified for heavy duty highly stressed applications.
The addition of nickel increases shock resistance and toughness whilst the chromium increases the material s hardenability giving it a uniformed hardness.
Download this datasheet as pdf en36a is a 3 2 nickel chromium high hardenability case hardening carburizing steel generally supplied in the annealed condition with a maximum brinell hardness of 255 rc26.
In particular medium to large cross sections.
When carburised and hardened core strengths of 850 1230 n mm are attainable.
Material technical standard of bs new standard ps970 1 1996 alloy steel 655m13 en36a data sheet bs 655m13 en36a chemical compositions 655m13 en36a mechanical properties from steelmaking esr melted blooming hot forging hot rolling heat treatment straightening 100 ultrasonic test cold working peeled or rough turned machining.
Values 0 13 0 20 0 45 3 50 0 80 0 025 0 025 as din bs 970 aisi nearest standard x3312 1 5752 14nicr14 655 m 13 en36a e9315 description chromium nickel case hardening steel for applications requiring excellent wear surface and high toughness and core strength.
100 ultrasonic test astm e2375 sae ams 2154 sep 1923 gb t 4162 en 10228 3.
All information in our data sheet is based on approximate testing and is stated to the best of our knowledge and belief.
Atlas 6587 low alloy steel bar complies with both 17crnimo6 din17210 and 18crnimo7 6 en 10084 both described under material number 1 6587.
When carburised and hardened cores strengths of 850 1230 n mm are attainable.
Chemical composition specification values in c si mn p s cr ni mo 0 15 0 21 0 40 0 50 0 90.
It is presented apart from contractual obligations and does not constitute any guarantee of properties or of processing or application possibilities in individual cases.